| Categories | Water Based Hydroxyl Acrylic Resin |
|---|---|
| Model Number: | WL-H152 |
| Certification: | ISO9001 |
| Place of Origin: | china |
| MOQ: | 5000KG |
| Payment Terms: | L/C, T/T |
| Supply Ability: | 500t/month |
| Delivery Time: | 14 work days |
| Packaging Details: | 200kg/drum |
| Brand Name: | WeiLi Resin® |
| Price: | Negotiable |
| Appearance: | Milky White Liquid |
| Non-volatile Matters(%): | 43±2 |
| Viscosity (mPa*s): | ≤500 |
| pH: | 7.0-8.0 |
| VOC(%): | <5 |
| Hydroxyl Value (mgKOH/g): | 108 |
| Density(g/cm3): | 1.047 |
| Package: | 200kg |
| Company Info. |
| Xiamen WangQin Chemical Technology Co., Ltd. |
| Verified Supplier |
| View Contact Details |
| Product List |
Water Dispersion Hydroxyl Acrylic ResinWL-H152 is two component PU resin, it is suggested to be used cooperatively with poly aliphatic isocyanate curing agent, through baking, it can maximize performance.water based hydroxyl acrylic dispersion can produce the same hardness, impact resistance and solvent resistance as solvent based polyurethane coating. PU coating made of WL-H152 is recommended to use in topcoat of metal or wood due to its paint film has excellent gloss, the construction method can be brushing, roll coating or spraying.
1, Product Composition:
Waterborne hydroxyl Acrylic Dispersion, Cosolvent, Neutralizing Agent, Water
2, Typical Data:
| Item | WL-H152 | Test Method |
| Appearance | Milky White Liquid | Visual Observation |
| Non-volatile Matters(%) | 43±2 | 30min@120℃ |
| Viscosity (mPa*s) | ≤500 | Rotational Viscometer |
| pH | 7.0-8.0 | PH Meter |
| VOC(%) | <5 | |
| Hydroxyl Value (mgKOH/g) | 108 | (For solid resin, theoretical value) |
| Density(g/cm3) | 1.047 | Densimeter |
3, Product Properties:
Self emulsifying process, emulsifier free.
Excellent shear stability, can be grinded with dispersions directly.
Good gloss, hardness and limit film thickness.
Excellent weather resistance, water resistance and aging resistance.
4, Instructions:
WL-152 can be diluted with deionized water to construction viscosity. The resin can help to wet pigments, so wetting agent may reduce PH valueof the coating system can always be adjusted by N. N-dimthylethanolamine, viscosity of the dispersion will increase as the PH value increases
WL-152 can be mixed with poly aliphatic isocyanate curing agent for preparing high-gloss top coating which can dry fast at room temperature ordry by force at 80"C. The activation period is about 3 hours if it is used with BAYHYDUR 304(NCO/OH=1. 4/1.0).
Construction equipments can be cleaned by water, alkaline detergent or water soluble solvent.
5, Product Properties Test:
| Gloss(60o)high gloss kind | >90 | Adhesion(grid) | 0 grade |
| Surface dry min(23o) | 15min | Adhesion(circle) | 1grade |
| Air dry 25o/h | 4h | Water resistance(23o) | 480h |
| Baking 65o/min | 65o,30min | Alkaline resistance (25o 0.1N NaOH) | 24h |
| Pot life(25o) | 4h | Acid resistance (25o 0.1N H2SO4) | 24h |
| Hardness(pencil) | 1H-2H | Gasoline resistance | 24h |
| Flexibility/mm | 1grade | Artificial aging resistance | 1000h Loss of gloss 30% |
| Impact resistance kg*cm | 50 | Q-sun,1200h | 1grade |
| Heat resistance | 105o | Continue 24h | 24h |
6, Storage:
It is suggested that the product should be stored in a cool and dry weak alkaline place. The quality guarantee period is 6 months, and the expiredproducts can still be used after passing the inspections.
7, Applications:
2KPU self-drying top coatings and amino-baking top coatings.
8, Note:
the specification is a general introduction to the products of our company. It will be adjusted with the product improvement Please contact with thecompany to obtain the latest product description.
|
Good Salt Spray Resistance Self-Crosslinking Modified Epoxy Resin For Metal Coating
1K Waterbased Hydroxyl Acrylic Resin,Good Metal Orientation,Car Refinishing
High Hardness Water Based Hydroxyl Acrylic Resin For Floor Coating
Water-based Hydroxypropyl Resin With Waterborne And Solvent Curing Agent For Metal Caoting
Water-based Hydroxy Acrylic Acid Similar To Covestro A145 For Large-area Flow Coating
Good Aluminium Orientatio Water-based Hydroxylated Acrylic Emulsion For Metal Coating
Repaintable Aqueous Hydroxyl Acrylic Dispersion For Metal And Wood Primer
Longer Potlife Water Based Hydroxyl Acrylic Dispersion For Heavy Equipment Painting
Ultra-long Pot Life Hydroxylated Acrylic Dispersion For Vehicle Interior Coatings
Water Based Hydroxyfunctional Polyacrylic Resin For Large Component Construction