| Categories | Water Based Hydroxyl Acrylic Resin |
|---|---|
| Brand Name: | WeiLi |
| Model Number: | WL-AD3940 |
| Certification: | ISO9001 |
| Place of Origin: | China |
| MOQ: | 5000KGS |
| Price: | Negotiable |
| Payment Terms: | T/T |
| Supply Ability: | 500TONS |
| Delivery Time: | 15 working days |
| Packaging Details: | plastic drum |
| hydroxyl value(%): | 3.9 |
| Advantage: | suitable for high temperature and low humidity environment |
| Feature: | could be used with solvent/water based curing agent |
| performance: | excellent water resistance（15days） |
| Impact (front/back cm kg): | 50/50 |
| Company Info. |
| Xiamen WangQin Chemical Technology Co., Ltd. |
| Verified Supplier |
| View Contact Details |
| Product List |
Product Introduction
It is a water-based hydroxylated acrylic dispersion, which is recommended to be used with solvent- based or water-based isocyanate curing agents to prepare water-based high-performance two- component polyurethane coatings, designed for topcoats on various metal substrates.
The resin has a hydroxyl content of WEI 3.9%, which is particularly suitable for construction environments with high temperature and low humidity. It can be used with an oily curing agent, which has a better cost-effectiveness.
Features: Excellent compatibility with solvent-based isocyanate curing agents, excellent water resistance, and long application period.
Physical Property
Appearance | Milky white liquid | Detection method |
Non-volatile matter (%) | 44±2 | GB/T 1725-2007 |
Viscosity (mPa·S) | 200-3000 | GB/T 21059-2007 |
PH | 7.5~8.5 | GB/T 9724-2007 |
hydroxyl value(%) | 3.9 | Based on solids |
The viscosity of the product is affected by the pH value, as the pH value increases, the viscosity and thixotropy will increase.
This resin can be used with an oily curing agent.
The following are the paint film properties measured after using a group of solvent curing agents
Item | WL-AD3940/TPA100 (Diluted by BGA) |
25℃/35% outdoor corridor Under breeze conditions | 60min |
| Surface drying time 14.5℃/60% outdoor corridor Under medium and high humidity conditions | 120min |
Water resistance at room temperature | 15 days |
Pencil hardness (baking) | H |
Bending resistance (mm) | <1 |
Impact (front/back cm kg) | 50/50 |
Effective opening period at 35℃ | 4h |
Special Tips
This material is complied according to our existing technology and experience, the technical advice provided is sincere, but it is not guaranteed to be used in all samples and formulations, all the data are for users reference only.
|
Good Salt Spray Resistance Self-Crosslinking Modified Epoxy Resin For Metal Coating
1K Waterbased Hydroxyl Acrylic Resin,Good Metal Orientation,Car Refinishing
High Hardness Water Based Hydroxyl Acrylic Resin For Floor Coating
Water-based Hydroxypropyl Resin With Waterborne And Solvent Curing Agent For Metal Caoting
Water-based Hydroxy Acrylic Acid Similar To Covestro A145 For Large-area Flow Coating
Good Aluminium Orientatio Water-based Hydroxylated Acrylic Emulsion For Metal Coating
Repaintable Aqueous Hydroxyl Acrylic Dispersion For Metal And Wood Primer
Longer Potlife Water Based Hydroxyl Acrylic Dispersion For Heavy Equipment Painting
Ultra-long Pot Life Hydroxylated Acrylic Dispersion For Vehicle Interior Coatings
High Performance Hydroxyfunctional Polyacrylic Dispersion With Weathering Resistance