| Categories | Solvent Based Hydroxyl Acrylic Resin |
|---|---|
| Brand Name: | WeiLi Resin® |
| Model Number: | SE6670M |
| Certification: | ISO9001 |
| Place of Origin: | China |
| MOQ: | 5000KG |
| Price: | Negotiable |
| Payment Terms: | L/C, T/T |
| Supply Ability: | 500t/month |
| Delivery Time: | 14 work days |
| Packaging Details: | 200kg/drum |
| Appearance: | clear and transparent |
| performance: | good leveling property |
| hydroxyl value: | 3.0% |
| Feature: | Excellent chemical resistance |
| Usage: | 2k Automobile Refinishing Paint |
| Type: | two-component polyurethane coatings |
| Company Info. |
| Xiamen WangQin Chemical Technology Co., Ltd. |
| Verified Supplier |
| View Contact Details |
| Product List |
SE6670M Solvent-Based Hydroxyl Acrylic Polyol Resin 2k Automobile Refinishing Paint
Product Introduction
SE6670M is a solvent-based acrylic polyol resin with 3.0% hydroxyl content (based on the theoretical calculation of non-volatile components). It is used to prepare solvent-based two-component polyurethane coatings mixed with aliphatic isocyanate curing agent. It is suitable for cement permeable paint, anticorrosive paint, PU finish paint and floor paint.
Physical Property
| Appearance | clear and transparent |
| Solid content | 63.0–67.0% |
| Color number | ≦ 1#(Fe-Co) |
| Acid value (mgKOH/g ) | 4.0-8.0 |
| Viscosity (25°C, NDJ rotational viscometer) | 4.0-7.0 Pa.s |
| flash point (°C) | 22 |
| hydroxyl value | 3.0% (based on the non-volatile components) |
| density (20°C) | 0.99-1.03 g/ml |
Performance
High gloss, good leveling property;
Excellent chemical resistance;
Fast drying speed, high hardness.
Application
It is mainly used in combination with Desmodur N75, N3390, N3600 and other curing agents, and can be used to prepare self-drying or low-temperature baking cement permeable paint, anticorrosive paint, PU finish paint and floor paint.
Storage
The resin should be stored indoors in original, unopened, undamaged container in a dry place at storagetemperature no more than 30ºC. Exposure to direct sunlight should be avoided.Under above mentioned storage condition, the shelf life ofthe resin will be 730 days after production.
Compatibility with resins and solvents
| SE6631 | + | SE6771 | + | xylene | + | 2-Butoxyethanol | + |
| SE6650 | + | SE6673 | + | S-100 | + | CAC | + |
| SE6790 | + | BAC | + | PMA | + | ||
| CYC | + | n-butanol | + |
Note: + means soluble/miscible; ○ means partially soluble/partially miscible; -means insoluble/incompatible.
Reference recipe
| Two-component (high gloss black paint) | diluent | ||
| (Part A) | |||
| SE6670M | 65 | xylene | 40 |
| Carbon black powder | 4 | toluene | 5 |
| BYK306 | 0.2 | BAC | 25 |
| EFKA3034 | 0.1 | PMA | 15 |
| BYK110 | 3 | CAC | 15 |
| 10%T-12 | 0.3 | ||
Special Tips
This material is complied according to our existing technology and experience, the technical advice provided is sincere, but it is not guaranteed to be used in all samples and formulations, all the data are for users reference only.
|
High Fullness Solvent Based Acrylic Resin For Motorcycle Finishing Coat
High Solid Low Viscosity Hydroxyl Acrylic Resin Excellent Weather Resistance
Excellent Adhesion Solvent Based Acrylic Resin For Metallic Substrates
High Gloss Hydroxyl Acrylic Resin Metallic Top Coatings Excellent Durability
PU Coatings Solvent Based Acrylic Resin , Eco Friendly Resin For Spectacle Frames
Steel / Plastics Weather Resistant Resin Durable Excellent Levelling Property
Flexible Solvent Based Acrylic Resin , Two Component Hydroxyl Acrylic Resins
Solvent Based Hydroxyl Functional Acrylic Resin For Automobile Refinishing Paint
Wide Compatibility Solvent Based Acrylic Resin , Rubber Primer Clear Acrylic Resin
Good Adhesion Solvent Based Products Floor Coatings Combining With Isocyanate Curing Agent