| Categories | Anti Corrosion Powder Coating |
|---|---|
| Brand Name: | TOPO |
| Model Number: | AC-RAL1007 |
| Certification: | CE, BV, ROHS |
| Place of Origin: | Ukraine |
| MOQ: | Negotiable |
| Price: | Negotiable |
| Payment Terms: | Western Union, MoneyGram, L/C, T/T |
| Supply Ability: | 400 T/Month |
| Delivery Time: | 7 days |
| Packaging Details: | Two-ply PVC bag inside with carton box, net weight 20/25kg |
| Color: | daffodil yellow |
| Components: | resin, pigment |
| Appearance: | fine powder |
| Adhesion: | 0 Grade |
| Packing: | Carton |
| Curing: | 180-200ºC,10 min-15 min |
RAL1007 daffodil yellow Anti Corrision powder coating for Electrical Household Appliances
It is specifically designed for meeting the requirement of super
anti-coccosive property.
Its outstanding gloss retention, durable color stability and
mechanical properties make it best to be applied to construction
materials, oil pipelines, boats, electrical appliances, metal
furnitures, decorations...
Compared with liquid paint, powder coating is more environmental friendly and economic. It can form a harder & thicker finish. Its excellent properties and attractive appearance of this product make it suitable for application to any other metal substrates.
| Property | Standard | Result |
| Film appearance & color | No unevenness and no color difference | |
| Adhesion | EN ISO 2409 (2mm) | Cross-cut rating Gt0 (100% adhesion) |
| Impact resistance | EN ISO 6272/ASTM D2794 | 50Kg/cm² without film cracking |
| Cupping test | EN ISO 1520 | Indentation depth in excess of 5mm without film cracking |
| Flexibility | EN ISO 1519 | Cylindrical Mandrel bending test, passes 2 mm |
| Film hardness | EN ISO 2815 | 1H - 2H by Pencil Hardness Test |
| Drilling, milling and sawing | No flaking of coating | |
| Neutral salt spray resistance | ASTM B117 | No blistering or loss of adhesion after 1000 hours |
| Humidity resistance containing SO2 | EN ISO 3231 | No infiltration exceeding 1 mm on both sides of the scratch after 30 cycles. |
| Humidity resistance | EN ISO 270-2 | No infiltration exceeding 1 mm on both sides of the scratch after 1000 hours. |
| Acetic acid salt spray resistance | ISO 9227 | After 1000 hours testing - maximum 16mm infiltration over a scratch length of 10cm |
| Accelerated weathering | DIN EN ISO 11507 (UVB - 313) | Cycle: 4 hours at 50 C UV and 4 hours at 40 C condensation. No chalking, excellent gloss retention and color stability after 300 hours testing. |
| Accelerated weathering | DIN EN ISO 11507 (UVA - 340) | Cycle: 8 hours at 60 C UV and 4 hours at 45 C condensation. No chalking, excellent gloss retention and color stability after 1000 hours testing. |
| Natural weathering test | ISO 2810 | No chalking, excellent gloss retention and color stability after 12 months exposure (angle of 5° to South). |
|
Indoor Lighting Anti Corrosion Powder Coating RAL 1001 Beige Color
Indoor Lighting Anti Corrosion Powder Coating RAL 1001 Beige Color
Metal Anti Corrosion Powder Coating Excellent UV Properties RAL 1002 Color
Metal Anti Corrosion Powder Coating Excellent UV Properties RAL 1002 Color
RAL 1004 Anti Corrosion Powder Coating For Metal Machinery Reinforcement
RAL 1004 Anti Corrosion Powder Coating For Metal Machinery Reinforcement
Geysers Anti Corrosion Powder Coating RAL 1006 Color 180-200ºC Curing
Geysers Anti Corrosion Powder Coating RAL 1006 Color 180-200ºC Curing
RAL 1011 Anti Corrosion Powder Coating For Aerospace Area 0 Grade Adhesion
RAL 1011 Anti Corrosion Powder Coating For Aerospace Area 0 Grade Adhesion