Brand Name: | MC silicone |
Model Number: | MCSIL-2020 |
Certification: | MSDS,SGS |
Place of Origin: | China |
MOQ: | 100kg |
Price: | Negotiable |
Payment Terms: | L/C, D/P, T/T, Western Union, |
Supply Ability: | 4000kg per day |
Delivery Time: | About 3-5 working days |
Packaging Details: | 25kg/kg, 550kg per pallet, 20 pallets per 20ft container |
Goods Description: | Silicone in Primary Forms |
HS Code: | 39100000 |
Cure Type: | Condensation Cure liquid Silicone Rubber |
Color: | White, (custom color) liquid Silicone Rubber |
Viscosity: | 22000 cps liquid Silicone Rubber |
Mix Ratio: | 100:2 liquid Silicone Rubber |
Working time: | 30-40 minutes |
Curing Time: | 4-6 Hours |
Hardness: | 20 shore A liquid Silicone Rubber |
Tensile Strength: | 3.8Mpa |
Tear strength: | 25N/mm |
shelf life: | 12months |
Company Info. |
MINGCHENG GROUP LIMITED |
Verified Supplier |
View Contact Details |
Product List |
20 Shore A Tin Cure Moulding Silicone Resin Crafts Mold Making RTV2 Liquid Silicone Rubber
Product Description
Silicone liquid rubber is is generally named as two-part room temperature sulfurated silicone rubber, which features an exceptional fluidity and good operability. When mixed with 2% curing agent, they can still be operated within 30 minutes, but will be formed after 4-6 hours. With resistance to deformation, high temperature, acid and alkali, and expansion.
Typical Properties of RTV-2 silicone liquid rubber
Item No. | Properties before curing | Curing | ||||||||
Part A | Part B | Part A+ Part B | Pot life at 250C | De-molding Time at 25℃ | ||||||
Appearance | Appearance | Ratio | Viscosity | |||||||
MCSIL-2020 silicone rubber | White | Clear | 100:2 | 22000±2000 cps | 30-40 mins | 4-6 hours | ||||
Properties after curing 24 hours | ||||||||||
Hardness Shore A | Tear strength | Tensile Strength | Elongation break (%) | Linear Shrinkage | ||||||
20 | 28-30 N/mm | 3.8 Mpa | 450-500 | 0.2-0.4% |
Various Applications of silicone liquid rubber
Various Applications of Silicone Liquid Rubber
Architectural Restoration
Concrete Casting
Gypsum Decorations
Resin Arts and Crafts
Candle and Soap
Staute & Scupltures
Wax Casting
Features of RTV-2 silicone liquid rubber
(1) high tensile & tear strength
(2) Low linear shrinkage
(3) free Curing agent
(4) brushing & pouring
(5) high duplication times
Operation Instructions of Silicone Liquid Rubber
Correct mixing ratio
Component A is silicone rubber, and component B is curing agent or
vulcanizing agent. Usually the mixing ratio will be 2-3%, e.g. to
100g silicone rubber should be added 2g catalyst and then mix them
thoroughly. (Note: the weight of the silicone and catalyst should
be weighed correctly).
Pouring the mixture and curing
Pour the misxed Part A base silicone and CA-30 curing agent as soon as possible onto the original,avoiding air entrapment.The catalyzed material will cure to a flexible rubber within 6 hours(or faster by different mixing ratio or room temperature),we advice you de-mold after 24 hours ,it is will improve the replicate times of silicone mold.
Package of RTV-2 Silicone Liquid Rubber
Part A base silicone: 25kg/drum or 200kg/drum
Part B CA30 Curing Agent: 800g/bottle, 1kg/bottle
Storage & Shelf life
When the silicone rubber is stored at or below 25℃ (77℉) with the original unopened containers, Silicone Base and Curing agent have a usable life of 12 months from the date of production. After 12 months stock, please use the Stir machine to mix the Part A silicone for some minutes, then the silicone can be used again, no influence for other performance.
![]() |