| Categories | ED Black Coating |
|---|---|
| Brand Name: | HAOLISEN |
| Model Number: | HLS-1701B/HLS-1701B |
| Certification: | IATF16949 , ISO9001 |
| Place of Origin: | Shanghai China （Mainland） |
| MOQ: | Negotiation |
| Price: | Negotiation |
| Supply Ability: | 200 Tons Per Day |
| Delivery Time: | 30-60 Days |
| Packaging Details: | 50kg、60 kg、200kg、1000kg packaging barrels |
| Performance: | Good anticorrosive |
| Cooperation case: | SANY,LION CHINA |
| main ingredients: | alcohol ether ;Titanium pigment |
| Application field: | Engineering mechanical |
| Company Info. |
| HLS Coatings （Shanghai）Co.Ltd |
| Verified Supplier |
| View Contact Details |
| Product List |
Engineering mechanical or the parts for the black electrophoretic paint
Product Introduction
1.HLS-1701BLB/HLS-1701B Black Cationic Epoxy Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd.
2.It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal, such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products and stainless steel sheet etc.
This product features shown below:
| Good stability of bath can adaptable for a longer updating cycle. | Coating fullness of good, better substrate hiding . | Strong anti-corrosion properties, good salt spray resistance workpiece edge. |
Main ingredients
| Additives: surface active agent, prevent shrinkage cavity agent | |
| Solvent: alcohol ether | Neutralizing agent: organic acid |
Filling tank proportion and method
Coating conditions
Experimental panel: phosphated cold-rolled steel plate
Tank temperature: 30-36℃
Pole ratio: A/C = 1/2 ~ 1/4
Distance of electrodes: 15cm
ED time: For full immersing 1-3 minutes ( 20 seconds soft start)
Baking conditions:(180-190)℃×(20-30)min (Keeping temperature of parts coated)
Product film performance
| Project | Indicator | Test standard | |
| Appearance | Normal / abnormal | Normal | Ocular estimate |
| Hardness | ≥ | 2H | GB/T 6739 |
| Cup drawing | mm ,≥ | 6 | GB/T 9753 |
| Adhesion | Level | 0 | GB/T 9286 |
| Flexibility | mm | 1 | GB/T 1731 |
| Impact | kg·cm | 50 | GB/T 1732 |
| Gloss | 60 | 50-80 | GB/T 9754 |
| Water resistance | h,(23±2)℃,≥ | 240 | GB/T 1733 |
| Acid resistance | h,(50g/L H2SO4),≥ | 72 | GB/T 9274 |
| Alkali resistance | h,(50g/L NaOH),≥ | 48 | GB/T 9274 |
| *Salt spray resistance | h,(film thickness ≥ 20μm) ,≥ | 1000 | GB/T 1771 |
* Note: The substrate use the Bonder standard phosphating steel panel, crossed out unidirectional expansion eclipse ≤ 2mm.
Customers in the engineering machinery
|
High - Light Epoxy ED Black Coating For Exterior Decorative Products
Matte Cationic Epoxy Electrocoat Paint , 3C Electronics Parts Cataphoresis Coating
High Weatherability Black Cathode Edp Coating With Uv Radiation Resiistance
Low Temperature Curing Black Electrophoresis Paint For Shock Absorber And Compressor
Eco Friendly ED Black Coating Water Based Paint High Anticorrosive Performance
Car Chassis Black Electrophoretic Paint Like Frame Bridge Plate Spring
Commercial Vehicles Skylight ED Black Coating With Kaolin Main Ingredients
Anti Shrinkage Black E Coat , Cathodic Electrocoating For Motorcycle Parts
Two Component ED Black Coating Low Temperature Curing For Car Shock Absorber
Anti Rust ED Black Coating , Edp Painting For Air Conditioning Compressor