Secar 71 Secar 68 Calcium Sulphoaluminate Cement Primary Binder

The Primary Binder In Mortars And Concretes Secar 71 Secar 68 Calcium Aluminate Cement

Calcium Aluminate Cement

SECAR® 71 is a versatile hydraulic binder with an alumina content of approximately 70%, which is designed to be used at temperatures in excess of1400°C.

SECAR® 71, a pure cement manufactured by the sintering process, contains only calcium aluminates. The high calcium aluminate content provides characteristics ideally suited for refractory applications where rapid hardening combined with excellent mechanical resistance and high temperature performance are required.

SECAR® 71 is the reference product for high technology deflocculated castable systems such as LCC, ULCC, shotcrete and pumpable refractories. Its controlled mineralogy gives the formulator great flexibility in castable design and also gives good

compatibility with micro silica.

Calcium aluminate cements do not release Calcium Hydroxide as a hydration product when used as the sole hydraulic compound in a formulation. This imparts good refractoriness and chemical resistance.

Specifications of Refractory cement Secar 71

Chemical constituents (% by XRF chemistry)
Al2O3	CaO	SiO2	Fe2O3
≥68.5	≥ 31.0	≥ 0.8	≥ 0.4

Blaine fineness: 3700-4500 cm2/g (ASTM C204)

Physical Properties (using EN-196 sand mortar)

 Flow at 30 min:  60% (ASTM C1437)

 Vicat Initial Set:  175 min.

 Vicat Final Set:  290 min

Modified ASTM C191 - Needle weight is 1000g, needle diameter

is 1.16 mm, samples immersed in water.

 Compressive strength (ASTM C349)

6 hr  1250 psi (8.6 MPa)

24 hr  4600 psi (31.7 MPa)

CH Refractories is cooperating with Chinese Secar agent, can supply you Secar cement with competitive price. If you need Secar cement, welcome to ask price.

Packaging & Shelf Life

SECAR® 71 is available palletized in 50 lb bags, 100 lb bags or 3000 lb. super sacks.

SECAR® 71 packaging is designed to protect it from humidity. However, as with all hydraulic binders, it is recommended that SECAR® 71 not be placed outdoors or in direct contact with the ground. When correctly stored in dry conditions, the properties of SECAR® 71

will remain within specification limit for at least 6 months. In most cases, its properties will be retained for over a year.

Zhengzhou Caihua Kiln Masonry Installation Co., Ltd. was established in 1984 in the brand of CH REFRACTORIES provides the highest quality of refractories and knowledge coupled with leading source of R&D advancements. Our seasoned team provides the expertise passion and attention to detail providing our customers the value-added service they need to succeed. 

CH REFRACTORIES is professional manufacturer of fire bricks, Mortar, Pre-cast, Pre shape, Insulation products, Castable, Functional Products for  Iron & Steel, Cement, Glass, Power & Petrochemical Industries.

Moreover, CH REFRACTORIES also manufacturing and exporting refractory cement A600 A700 A900 CA70, Bauxite and other refractories raw material to all of the world.

CH REFRACTORIES manufacturing plant is located in the  Xinmi City that is rich refractory raw materials and coal storage. Unique conditions provide extremely convenient conditions for the production and development of refractories.

CH REFRACTORIES  has 158 middle-level technical titles and 38 senior technical titles. The company has strong technical strength and has established stable technical cooperation with Luoyang Refractory Materials Research Institute, Zhengzhou University High Temperature Research Institute, Beijing University of Science and Technology, Northeastern University, Anshan Iron and Steel College and other institutions of higher learning. It is the Beijing University of Science and Technology. Production, teaching and research bases.

CH REFRACTORIES with Advanced technical equipment, advanced raw material preparation system, hybrid electronic batching vehicle, 750 type mixing and mixing machine. 

Molding equipment: 2 sets of 1000 tons of brick presses, 4 sets of 630 tons of brick presses, 400 tons of 14 sets of brick presses, 22 sets of 315 tons of brick presses, 2 sets of 160 tons of brick presses and 8 sets of 60 tons of brick presses.

The firing equipment includes: a high temperature shuttle kiln, a high temperature 180 m tunnel kiln, a high temperature 120 m tunnel kiln and a medium temperature tunnel kiln.