| Categories | Electrophoretic Coating |
|---|---|
| Brand Name: | HAOLISEN |
| Model Number: | HS-6600LB/HS-6060A |
| Certification: | IATF16949 , ISO9001 |
| Place of Origin: | Shanghai China （Mainland） |
| MOQ: | Negotiation |
| Price: | Negotiation |
| Supply Ability: | 200 Tons Per Day |
| Delivery Time: | 30-60 Days |
| Packaging Details: | 50kg、60 kg、200kg、1000kg packaging barrels |
| main ingredients: | organic acid ;antirust pigment |
| Application field: | microwave oven |
| Performance: | Color uniformity |
| Cooperation case: | Galanz |
| Company Info. |
| HLS Coatings （Shanghai）Co.Ltd |
| Verified Supplier |
| View Contact Details |
| Product List |
Electrophoretic coating for domestic microwave oven
Product Introduction :
HS-6060ALB/HS-6600 White Cationic Epoxy Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd.
It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal, such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products, zinc-aluminum alloy sheet and stainless steel sheet etc.
This product features shown below:
Excellent leveling coating,good bonding force and compatibility with plastic powder.
Strong anti-corrosion properties, good salt spray resistance workpiece edge.
Good stability of bath can adaptable for a longer updating cycl
Main ingredients:
Pigment: titanium dioxide, kaolin,antirust pigment | Neutralizing agent: organic acid |
Additives: surface active agent, prevent shrinkage cavity agent,resistance to yellowing agent | |
Product quality data
| Project | Technical data | Test standard | ||
| Resin (HS-6060ALB) | White Paste (HS-6600) | |||
| pH | 25℃ | 6.0±1.0 | —— | GB/T 9724 |
| Conductivity | 25℃, μs/cm | 1400±400 | —— | HG/T 3334 |
| Appearance | —— | Milky white liquid | White viscous liquid,no agglomeration | Visual |
| Storage stability | No stratified state, and there were no obvious difference compared to before storage | In 5-35 ℃ temperature 1 year | ||
Note: pH, conductivity measurement in the resin/pure water = 1:1 dilution
Filling tank proportion and method
⑴ Bath preparation
Ratio:
Resin 750.00-1000.00
Paste 250.00
DI water 1900.00-2200.00
Total 3 3025.00-3575.00
⑵ Ripening conditions
Sample quantity: 3000-4000g
Container: 5L (Diameter 16cm)
Tank temperature:28-30 ℃
Time: 24～48Hr
Mixed conditions: impeller diameter 8cm (speed 200rpm)
(3) Coating conditions
Experimental panel: phosphated cold-rolled steel plate
Tank temperature: 28-34 ℃
Pole ratio: A/C = 1/2 ~ 1/4
Distance of electrodes: 15cm
ED time: For full immersing 1-3 minutes ( 20 seconds soft start)
Baking conditions:(165-175)℃×(20-30)min (Keeping temperature of parts coated)
Customers in the microwave oven industry:
|
Outdoor Furniture Electrolysis Painting , Ced Painting Excellent Adhesion
Automobile Door Ed Black Coating , Anti Pollution Edp Paint Water Dispersed Resin
Black Cationic Epoxy Electrophoretic Coating For Automobile Cover Industry
Black Electrophoretic Coating Good Uniformity For Automobile Shock Absorber
Household Refrigerator Cationic Electrodeposition Paint With Surface Active Agent Additives
Domestic Washing Machine Epd Coating , Eco Friendly Cationic E Coat Paint
Water - Borne Electrophoretic Coating For Domestic Air Conditioning Industry
Car Seat Electrophoretic Painting , Cationic Epoxy Black E Coat Non - Hazardous
Automobile Wheel Hub Cationic Electrophoretic Coating Non - Inflammable And Explosive
Car Doors Cathodic Electrodeposition ED Black Coating Anti Shrinkage