| Brand Name: | HAOLISEN |
| Model Number: | HL-1607LB/HLS-1701A |
| Certification: | IATF16949 , ISO9001 |
| Place of Origin: | Shanghai China （Mainland） |
| MOQ: | Negotiation |
| Price: | Negotiation |
| Supply Ability: | 200 Tons Per Day |
| Delivery Time: | 30-60 Days |
| Packaging Details: | 50kg、60 kg、200kg、1000kg packaging barrels |
| Application field: | auto parts |
| Performance: | film smooth |
| Cooperation case: | LEAR,WANXIANG |
| main ingredients: | organic acid ; alcohol ether |
| Pigment:: | carbon black, kaolin, antirust pigment |
| Company Info. |
| HLS Coatings （Shanghai）Co.Ltd |
| Verified Supplier |
| View Contact Details |
| Product List |
Electrophoretic coating for auto parts industry
Product Introduction
HL-1607LB/HLS-1701A Black Cationic Epoxy Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd. It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal, such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products and stainless steel sheet etc.
This product features shown below:
The bath has strong anti-shrink age andanti-pollutionability.
Coating fullness of good,better sub strate hiding.
Strong anti-corrosion properties, good salt spray resistance workpiece edge.
The appearance of the coating is flat, delicate, smooth, uniform high gloss.
Main ingredients
| Matrix resin: | Acrylic modified epoxy resin |
| Pigment: | carbon black, kaolin, antirust pigment |
| Additives | surface active agent, prevent shrinkage cavity agent |
Product quality data
| Project | Technical data | Test standard | ||
| Resin (HL-1607LB) | Black Paste (HLS-1701A) | |||
| Appearance | —— | Milky white liquid | Black viscous liquid,no agglomeration | Visual |
| pH | 25℃ | 6.0±1.0 | —— | GB/T 9724 |
| Conductivity | 25℃, μs/cm | 1400±600 | —— | HG/T 3334 |
| Storage stability | No stratified state, and there were no obvious difference compared to before storage | In 5-35 ℃ temperature 1 year | ||
Note: pH, conductivity measurement in the resin/pure water = 1:1 dilution
Product film performance
| Project | Indicator | Test standard | |
| Appearance | Normal / abnormal | Normal | Ocular estimate |
| Hardness | ≥ | 2H | GB/T 6739 |
| Cup drawing | mm ,≥ | 6 | GB/T 9753 |
| Adhesion | Level | 0 | GB/T 9286 |
| Flexibility | mm | 1 | GB/T 1731 |
| Impact | kg·cm | 50 | GB/T 1732 |
| Gloss | 60 | 50-80 | GB/T 9754 |
| Water resistance | h,(23±2)℃,≥ | 240 | GB/T 1733 |
| Acid resistance | h,(50g/L H2SO4),≥ | 72 | GB/T 9274 |
| Alkali resistance | h,(50g/L NaOH),≥ | 72 | GB/T 9274 |
| *Salt spray resistance | h,(film thickness ≥ 20μm) ,≥ | 1000 | GB/T 1771 |
* Note: The substrate use the Bonder standard phosphating steel panel, crossed out unidirectional expansion eclipse ≤ 2mm.
Customer production site:
|
AAU Hydrophobic Nano One Coating System Container Paint
Colorful Epoxy Acrylic Electrocoat , Fine Electrocoating No Agglomeration
Automobile Body Industrial ED Paint Good Salt Spray Resistance Workpiece Edge
Smooth Cationic Electrodeposition Paint Excellent Leveling Coating For Hardware Tool Industry
Black Electrophoresis ED Paint High Hardness No Agglomeration For Galvanized Steel Sheet
Film Smooth Grey Cationic Epoxy Electrocoat , E Coated Steel Anti Corrosion Paint
High Throwing Power Electrophoresis Coating , White Ecoat Car Coating 0.25-0.35 P/B
Engineering Machinery Electrophoretic Painting With Titanium Pigment / Carbon Black Ingredients
High Solid Content Electrophoretic Coating For Agricultural Machinery Industry
Corrosion Resistance ED Paint for Flange in Automobile Chassis Industry